Title: TO STUDY THE WEAR RESISTANCE FOR THE TITANIUM CARBIDE-NiMo
_____________________________________________________________________________
Title: |
TO STUDY THE WEAR RESISTANCE FOR THE TITANIUM CARBIDE-NiMo |
Author Name: |
M.Yugandhar , R.Satheesh , N.Sathish Kumar , D.Raju, D.Pavan Teja |
Abstract: |
Three body abrasion in the present study, TiC–NiMo composites were remilled to particle size of 250–315 μm and used as reinforcements for NiCrBSi
alloy by plasma transferred arc hard facing process. The manufactured hard facing alloy was characterised in terms of microstructure, mechanical properties and
abrasive wear resistance. Deposition results indicate good quality thick coating with uniform distribution of hard cermet (TiC–NiMo) particles in the matrix, minimum
level of hard particle dissolution and low porosity of the hard facing. Cermet particles remain in initial form and consist of agglomerates (TiC and (Ti,Mo)C grains)
embedded into Ni-based matrix. The mechanical properties of the TiC and (Ti,Mo)C phases measured by nano indentation are very similar exhibiting a narrow
distribution. The nano-scratching test reveals excellent bonding between the matrix and cermets in the hard facing. No crack propagation was found in the interface
matrix/hard phase region. The abrasive wear results ensure the promising features of TiC–NiMo reinforcements for Ni-based alloys. Produced coatings showed
excellent performance under high-stress abrasion with wear values lower than for industrially used WC/W2C reinforced coatings.
|